发表刊物：SCIENCE CHINA-PHYSICS MECHANICS & ASTRONOMY

收录刊物：Scopus、SCIE、EI

卷号：55

期号：12

页面范围：2367-2371

ISSN号：1674-7348

关键字：bulk metallic glasses; glass-forming ability; mechanical properties; Zr-Al-Ni alloys

摘要：The thermal stability, glass-forming ability (GFA) and mechanical properties of Zr60Al15Ni25-x TM (x) (TM = Cu, Fe and Co, x = 0-10) bulk metallic glasses (BMGs) were systematically investigated. Additional 5-10 at.% Cu greatly enhances the thermal stability and GFA of the base alloy. Zr60Al15Ni15Cu10 BMG exhibits the largest supercooled liquid region of 104 K and critical diameter of 18 mm. However, addition of 5-10 at.% Fe or Co decrease the thermal stability and GFA. In addition, the plasticity of the BMG can be improved by adding of Cu, while the strength is decreased slightly. Zr60Al15Ni20Cu5 BMG has the largest plastic strain of 5.5% with a yield stress of 1755 MPa and Young's modulus of 83 GPa. Addition of Co brings an increase of strength but a lower of plasticity, and additional Fe reduces the strength and plasticity simultaneously.