发表刊物：JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE

收录刊物：SCIE、EI

卷号：26

期号：12

页面范围：6140-6148

ISSN号：1059-9495

关键字：Cr-Ni-Mo steel; hot compression; kinetics; static recrystallization

摘要：A series of two-pass hot compression tests were conducted on Gleeble-1500 thermo-mechanical simulator to investigate the static recrystallization (SRX) behavior of a medium-carbon Cr-Ni-Mo alloyed steel 34CrNiMo. The compression tests were performed at a deformation temperature range of 950-1150 A degrees C, a strain rate range of 0.1-3.5 s(-1), and an interval time range of 1-100 s. The experimental flow stress curves and microstructural observation indicate that deformation temperature, pass interval time, strain rate, and pre-strain have significant influences on the recrystallization behavior of 34CrNiMo steel. It is identified that the softening fraction increases with the increasing deformation temperature, pre-strain, and interval time, while it decreases with the increasing strain rate. Based on the experimental data, the SRX kinetics equations of 34CrNiMo steel were developed. And the calculated results are in good agreement with the experimental ones, which demonstrates that the established equations can be used to describe the SRX behavior of 34CrNiMo steel at elevated temperatures.