- Synthesis and characterization of Cu+/ MIL-100(Fe) with enhanced catalytic performance for NH3-SCR
- 点击次数：
- 论文类型： 期刊论文
- 发表时间： 2018-01-02
- 发表刊物： FERROELECTRICS
- 收录刊物： SCIE、EI
- 卷号： 522
- 期号： 1
- 页面范围： 20-28
- ISSN号： 0015-0193
- 关键字： DeNOx catalysts; selective catalytic reduction; Cu+; MIL-100(Fe); copper loading; MOFs; TB34; A
- 摘要： A mesoporous MIL-100 (Fe) loaded with Cu+ species was synthesized using a hydrothermal method and its denitrification (deNOx) capability for NH3-SCR process was investigated. From X-Ray diffraction (XRD), hydrogen temperature programmed reduction (H-2 -TPR) and X-ray photoelectron spectroscopy (XPS) results, it was concluded that the Cu+ has been successfully introduced into the framework structure. Moreover, it was found that copper species play a significant role to promote NO reduction activity of Cu+/ MIL-100(Fe) and NO conversion increased with copper amount. Compared with MIL-100(Fe), Cu+/MIL-100(Fe) achieves a 16% increase in the maximum catalytic efficiency at 300 degrees C, suggesting a favorable interaction between metallic copper and iron active sites.
上一条： Hollow porous zinc cobaltate nanocubes photocatalyst derived from bimetallic zeolitic imidazolate frameworks towards enhanced gaseous toluene degradation.
下一条： Construction of p-n heterojunction beta-Bi2O3/BiVO4 nanocomposite with improved photoinduced charge transfer property and enhanced activity in degradation of ortho-dichlorobenzene