摘要：With an aim of developing high quality in situ TiB2 reinforced aluminium foundry alloy based composites, the conventional direct synthesis method was modified into a two-step route. In step one we optimized the halide salt route to fabricate in situ TiB2 particulate reinforced aluminium matrix composites and in step two we investigated the effects of the Al-5wt.% TiB2 composite, as a "master composite", on strengthening the practical foundry alloys. The in situ formed TiB2 particles play two roles while strengthening the composites: (1) The grain refinement effect that improves the quality of the alloy matrix; and (2) The interactions between the hard particulates and the matrix add extra increment to the material strength. In different alloy systems, TiB2 may play distinct roles in these two aspects (figure 1). Further analysis of the strengthening mechanisms shows that particle agglomeration behaviour during solidification is responsible for the latter one. The present work details the role of TiB2 in strengthening TiB2 reinforced aluminium casting composites.