发表刊物：MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING

收录刊物：SCIE、EI、Scopus

卷号：644

页面范围：425-430

ISSN号：0921-5093

关键字：Aging behavior; Microstructure; Mechanical properties

摘要：In the present work, the combining effects of TiB2 and La on the aging behavior of A356 alloy were investigated by comparing microstructures and age-hardening curves. The results demonstrated that, with the addition of TiB2, the density of precipitates upon aging is increased with a smaller size due to the increased dislocation density caused by the coefficient mismatch of thermal expansion between the matrix and reinforcements, therefore significantly increasing the aging hardness of the matrix. La helps to refine the SDAS of the alpha-Al grains and disperse the TiB2 particles and leads to an acceleration in the aging kinetics which shortens the peak-aged time by some 30 min based on the existence of TiB2, further improving the aging precipitation hardening. Further, it was also noted that the La alloyed composite achieved a superior tensile property due to the improved aging precipitation strengthening. (C) 2015 Elsevier B.V. All rights reserved.