点击次数：

论文类型：期刊论文

发表时间：2012-01-15

发表刊物：JOURNAL OF ALLOYS AND COMPOUNDS

收录刊物：SCIE、EI

卷号：511

期号：1

页面范围：45-49

ISSN号：0925-8388

关键字：Metals; Casting; Al-Ti-B master alloy; Grain refinement

摘要：Al-Ti-B refiners with excess-Ti perform adequately for wrought aluminum alloys but inefficiently in the case of foundry alloys. The high content of silicon in the latter, which forms silicides with Ti and severely impairs the refining potency of the nuclei, is known to be responsible for the poor performance. Hence, new grain refiners, such as Al-3B and Al-3Ti-3B master alloys with excess-B have been developed with well documented advantages for Al-Si alloys. It is very desirable to involve TiAl(3) particles in the Al-3Ti-3B master alloy to maximize its grain refining efficiency. However, fading phenomenon is a key drawback for application of the TiAl(3)-containing refiners in aluminum foundry. In the present work, new Al-3Ti-3B grain refiners, containing TiB(2), AlB(12) and TiAl(3) particles were developed with an aim to prolong the acting time after inoculation. The results showed that inoculation of Al-7Si alloy with thus meliorated Al-3Ti-3B grain refiner has produced a fine grain structure which was approximately maintained up to 30 min. (C) 2011 Elsevier B. V. All rights reserved.