论文类型： 期刊论文

发表时间： 2018-01-24

发表刊物： MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING

收录刊物： SCIE、EI

卷号： 713

页面范围： 112-117

ISSN号： 0921-5093

关键字： Long-period stacking-ordered structure (LPSO); Nanoscale deformation behavior; Deformation mechanism; Magnesium-rare earth alloy

摘要： The nanoscale deformation behavior of high strength (240 MPa)-high ductility (21.4%) combination Mg-rare earth alloy with long-period stacking-ordered structure was studied via nanoindentation and electron microscopy, and the behavior compared with the low strength (65MPa)-good ductility (15%) alloy without LPSO structure. In non-LPSO alloy, basal < a > slip mainly occurred, while in LPSO-containing alloy, the LPSO changed the deformation mechanism to extensive non-basal < c +a > slip and deformation twinning. The intrinsic good plasticity of LPSO and its impact on the deformation mechanism of Mg matrix contributed to superior mechanical properties and nanoscale deformation behavior of Mg-rare earth alloys, without compromising the ductility.