Effect of neodymium, gadolinium addition on microstructure and mechanical properties of AZ80 magnesium alloy

点击次数:

发表时间:2019-03-13

论文类型:期刊论文

发表时间:2016-06-01

发表刊物:JOURNAL OF RARE EARTHS

收录刊物:SCIE、EI、ISTIC

文献类型:J

卷号:34

期号:6

页面范围:632-637

ISSN号:1002-0721

关键字:AZ80 alloy; Nd; Gd; microstructure; mechanical properties; rare earths

摘要:The microstructure and mechanical properties of AZ80 magnesium alloys with varying Nd, Gd contents were investigated. The results revealed that the as-cast microstructure of AZ80 alloy was composed of alpha-Mg matrix and divorced eutectic beta-Mg17Al12 phases. The fraction of Mg17Al12 phase was reduced when 0.6 wt.% Nd was added, and new rod-shaped Al11Nd3 phase and small block-shaped Al-Nd-Mn phase appeared. With Gd addition, the Gd elements mixed with Nd to form rare earth phases. New block-shaped Al2Gd and Al2Nd phases which were collectively called Al2RE phases were observed in the microstructure with more than 0.6 wt.% Gd addition. Moreover, the addition of Gd could promote the precipitation of block-shaped Al2RE phase, and inhibit the original rod-shaped Al11Nd3 phase. The AZ80-0.6Nd-0.6Gd alloy exhibited the optimal mechanical properties among all the experimental alloys, in which the tensile strength, yield strength and elongation were 215, 145 MPa and 8.33%, respectively.

上一条: Microstructures and properties of rapidly solidified Cu90Zr10-xAlx alloys

下一条: 铜模铸造Cu99Zr0.5Al0.5合金微观组织及时效工艺

赞:

辽ICP备05001357号 地址:中国·辽宁省大连市甘井子区凌工路2号 邮编:116024
版权所有:大连理工大学
访问量:

开通时间: ..

最后更新时间: ..