点击次数：

论文类型： 期刊论文

发表时间： 2008-12-01

发表刊物： TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA

收录刊物： SCIE、EI、ISTIC、Scopus

卷号： 18

期号： SPEC. ISSUE 1

页面范围： S96-S100

ISSN号： 1003-6326

关键字： Mg-Li-Al alloys; electromagnetic stirring (EMS); solution treatment; artificial aging; hardness

摘要： The effects of external fields such as electromagnetic field on the structure and heat treatment behavior of Mg-Li-Al alloys were studied. Mg-8Li-3Al alloys cast with and without electromagnetic stirring were used for solution treatment and aging treatment. Experimental results show that the dendritic arms are broken and a large quantity of equiaxed grains appear in the microstructure of specimens with electromagnetic stirring (EMS). With the increase of the quenching temperature(150-350 degrees C), the solution of Mg and Al in solid beta phase increases, and the Brinell hardness of the alloy increased as well. Aging peak and over aging happen because theta(MgLi(2)Al) which precipitates in the beta matrix and strengthens the alloy is unstable and transforms to stable AlLi phase. Aging curves of EMS specimens change in a smaller amplitude.