Study of the stability of n-diamond

点击次数:

论文类型: 期刊论文

发表时间: 2004-05-05

发表刊物: JOURNAL OF PHYSICS-CONDENSED MATTER

收录刊物: Scopus、SCIE、EI

卷号: 16

期号: 17

页面范围: 2991-2994

ISSN号: 0953-8984

摘要: Powders of n-diamond can be synthesized by pyrogenation of carbon black and nanometre-sized iron catalyst at atmospheric pressure and at a temperature of 1100degreesC. The stability of n-diamond was investigated with x-ray diffraction, thermal gravimetric analysis and differential thermal analysis. The results indicated that n-diamond was a metastable phase: it can decompose at room temperature slowly. Thermal decomposition of n-diamond begins at 150degreesC and is complete at 400degreesC, and the decomposition of n-diamond was an exothermic reaction.

辽ICP备05001357号 地址:中国·辽宁省大连市甘井子区凌工路2号 邮编:116024
版权所有:大连理工大学