Technical parameters in electromagnetic continuous casting of aluminum alloy

点击次数:

论文类型: 期刊论文

发表时间: 2003-04-01

发表刊物: TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA

收录刊物: SCIE

卷号: 13

期号: 2

页面范围: 365-368

ISSN号: 1003-6326

关键字: continuous casting; electromagnetic field; temperature field; casting speed; aluminum alloy

摘要: The temperature field of aluminum ingot during electromagnetic continuous casting was calculated by the numerical method, and the effects of cooling water strength, position of the cooling water holes and pouring temperature as well as induction heat on casting speed, were studied. The results show that among the technical parameters the distance from the position of the cooling water holes to the bottom of the mold is the most important factor, whose change from 20 mm to 15 mm and from 15 min to 10 mm causes the setting rate increasing respectively by 0.14 mm/s and 0.3 mm/s. The calculated results also agree with the experiment well. The simulation program can be used to determine technical parameters of electromagnetic casting of aluminum ingot effectively.