点击次数：

论文类型：期刊论文

发表时间：2007-01-01

发表刊物：JOURNAL OF REINFORCED PLASTICS AND COMPOSITES

收录刊物：SCIE、EI

卷号：26

期号：1

页面范围：15-24

ISSN号：0731-6844

关键字：phenoxy resin; polyurethane prepolymer; tensile strength; breaking extension; heat resistance

摘要：Phenoxy resin reacted with a toluene diisocynate-terminated polyurethane prepolymer forming a reinforced thermosetting plastic by static casting. We investigated the effects of the process conditions including crosslinking time, crosslinking temperature, and isocyanate index (1) on the mechanical property and heat resistance of the crosslinked product. Fourier transform infrared (FTIR), thermogravimetric analyzer (TGA), and a material testing machine were used to characterize and test the reinforced phenoxy resin. The results show that the maximum tensile strength is 71.8, 63, 41.9 MPa and breaking extension is 6.3%, 325%, 418.8% in I of 0.04, 0.16, 0.28, respectively, under the conditions of optimal crosslinking temperature of 100 degrees C and appropriate crosslinking time of 0.5-2h. The heat resistance of crosslinked phenoxy resin deteriorates with the increase of I. The all-round properties are optimum in I of 0.16 and isocyanate index decides the reinforced product property.