Physical model of stress and deformation microstructures in AISI 304L austenitic stainless steel induced by high-current pulsed electron beam surface irradiation

点击次数:

论文类型:期刊论文

发表时间:2008-01-01

发表刊物:ISIJ INTERNATIONAL

收录刊物:SCIE、EI

卷号:48

期号:2

页面范围:235-239

ISSN号:0915-1559

关键字:AISI 304L austenite stainless steel; HCPEB; deformation microstructures; stress; twin lamellae

摘要:AISI 304L austenite stainless steel was irradiated by a high-current pulsed electron beam (HCPEB) source in different process. The deformation microstructures were investigated by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The relationship between stress characteristic and the microstructures has been established. The current numerical simulations of the thermal-mechanical process of HCPEB treatment were also reviewed comparing with the present experimental results. Our experimental results suggest that the value of the stress induced by HCPEB is between 10(2)-10(3) MPa or even larger. This stress results in the change of microstructure of the irradiated material in deeper region beneath the surface. According to the experimental results, a new physical model of the thermal-stress process and related modification mechanism as a result of HCPEB irradiation has been developed.