论文名称:Facile Synthesis of Double-Layer-Constrained Micron-Sized Porous Si/SiO2/C Composites for Lithium-Ion Battery Anodes 论文类型:期刊论文 发表刊物:ACS APPLIED MATERIALS & INTERFACES 收录刊物:EI、SCIE 卷号:11 期号:41 页面范围:37732-37740 ISSN号:1944-8244 关键字:porous Si; spherical coral-like structure; porous Si/SiO2/C; electrical performance; lithium-ion batteries 摘要:Advanced Si-based anode materials with nano-sized porous structures and constrained coating layers present attractive prospects for lithium-ion batteries. A brand-new design of double-layer-constrained micron-sized (>20 mu m) porous Si/SiO2/C is proposed through facile synthesis processes using cheap Al-Si alloy as feedstock. The three-dimensional spherical coral-like porous Si structure is composed of primary Si (as a supporting framework), eutectic Si rods, and uniformly distributed conductive element Al, which is beneficial for providing void space and uniformly conductive sites. A 4 nm SiO2 thin layer is introduced on the surface of porous Si structure using preoxidation treatment, which has the effect to constrain the volume expansion of Si. The outer C layer can further improve the electrical conductivity and structural stability. The discharge and charge capacities of the porous Si1/SiO2/C composite are 933.3 and 929.2 mAh/g at 0.1 A/g after 100 cycles, respectively. The charge attenuation rate of porous Si1/SiO2/C in each loop is only 0.08%, and the lithium-ion diffusion coefficient of this composite is 4.20 X 10(-12) cm(2).s(-1/2). 发表时间:2019-10-16