论文类型:期刊论文
发表时间:2015-07-01
发表刊物:JOURNAL OF ELECTRONIC MATERIALS
收录刊物:SCIE、EI、Scopus
卷号:44
期号:7
页面范围:2331-2339
ISSN号:0361-5235
关键字:Fe-Ni-(Cr) alloys; mechanical alloying; microwave absorption; magnetic and dielectric loss
摘要:The microwave-absorption properties and microstructures of Fe-Ni and Fe-Ni-Cr alloys prepared by mechanical alloying were investigated in the frequency range 2-18 GHz. Other properties were studied by scanning electron microscopy, x-ray diffractometry, vibrating sample magnetometry, and transmission line theory. Dependence of reflection loss (RL), electromagnetic properties (permeability mu and permittivity epsilon), magnetic and dielectric loss tangent, impedance matching, and absorber thickness (d) on milling time is discussed. The alloy powders had excellent microwave-absorption properties in the frequency range 7 to 14 GHz. The minimum RL, the frequency at which the RL is minimum, and the bandwidth (RL < -10 dB) all depend on milling time and d. Introduction of Cr affected the RL of the powders, especially the minimum RL of -19.8 dB at 7.2 GHz for Fe-Ni-Cr powder milled for 90 h (compared with -22 dB at 9.9 GHz for Fe-Ni powder milled for the same time), suggesting that the Fe-Ni-Cr alloy could be a promising candidate as a microwave-absorbing filler at low frequencies. This may help broaden the range of microwave-absorbing materials.