发表刊物:JOURNAL OF ALLOYS AND COMPOUNDS
收录刊物:SCIE、EI
卷号:454
期号:1-2
页面范围:340-346
ISSN号:0925-8388
关键字:carbon black; barium titanate; compound particle; electric conductivity; complex relative electromagnetic constants; microwave absorption
摘要:Nanocrystalline carbon black/barium titanate compound particle (CP) was synthesized by sol-gel method. The phase structure and morphology of compound particle were investigated by X-ray diffraction (XRD), transmission electron microscope (TEM) and Raman spectrum measurements, the electroconductivity was test by trielectrode arrangement and the precursor powder was followed by differential scanning calorimetric measurements (DSC) and thermal gravimetric analysis (TGA). In addition, the complex relative permittivity and permeability of compound particle were investigated by reflection method. The compound particle/epoxide resin composite (CP/EP) with different contents of CP were measured. The results show barium titanate crystal is tetragonal phase and its grain is oval shape with 80-100 nm which was coated by carbon black film. As electromagnetic (EM) complex permittivity, permeability and reflection loss (RL) shown that the compound particle is mainly a kind of electric and dielectric lossy materials and exhibits excellent microwave absorption performance in the X- and Ku-bands. (C) 2007 Elsevier B.V. All rights reserved.