Using infrared thermography in effect evaluation of heat treatments on martensite steel

点击次数:

论文类型:期刊论文

发表时间:2012-01-01

发表刊物:Advanced Science Letters

收录刊物:Scopus

卷号:16

期号:1

页面范围:305-308

摘要:Experimental tests were carried out to study the effect of heat treatments on the microstructure and mechanical behavior of martensitic steel. Fatigue limits of the virgin and heat-treated martensitic steels were determined using the infrared thermography, achieving a good prediction. The external temperature increment was closely linked with the internal microstructural changes. The characteristics of the fracture surface were carefully observed by SEM, and accordingly it was found that fatigue cracks initiated from the specimen corner. The results show that the improvement of the mechanical properties of martensite was due to the formation of fine tempered martensite and second phase particles. ? 2012 American Scientific Publishers. All rights reserved.