点击次数：

论文类型：会议论文

发表时间：2015-01-01

收录刊物：CPCI-S、SCIE

卷号：39

页面范围：62-67

关键字：Polyimide; Flourene; Gas separation properties; Solubility; Structure and properties

摘要：The six kinds of polyimides(PIs) containing fluorene units were prepared from 9,9'-bis(4-aminophenyl)fluorene(BAF) with various dianhydrides including 2,2'-bis-(3,4-dicarboxyphenyl)hexafluoropropane dianhydride(6FDA), 3,3',4,4'-biphenyltetracarboxylic dianhydride(BPDA), 4,4'-oxydiphthalic anhydride(ODPA), 3,3', 4,4'-biphenyltetracarboxylic dianhydride(BTDA), pyromellitic dianhydride(PMDA) and 1,2,3,4-cyclobutanetetracarboxylic dianhydride(CBDA) via chemical imidization. Wide-angle X-ray diffractograms revealed that the polymers were amorphous. Most of the polyimides exhibited good solubility and could be readily dissolved in various solvents such as N-Methyl-2-pyrrolidone(NMP), N,N-dimethylacetamide(DMAc), N,N-dimethylformamide(DMF), and so on. The polyimide was thermally treated at 300 degrees C, 420 degrees C and 550 degrees C for further carbonization. Gas permeation properties for O-2 and N-2 of the PI-BPDA and PI-CBDA membranes were investigated. The permeability coefficients and selectivity for O-2 and N-2 of polyimide were obtained. With the increase of thermal treatment temperature, the permeability for O-2 and N-2 of polyimides increased, but the selectivity decreased. The gas separation mechanism for O-2 and N-2 was mainly molecular sieving.