Indexed by:期刊论文

Date of Publication:2013-12-01

Journal:JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE

Included Journals:SCIE、EI、Scopus

Volume:22

Issue:12

Page Number:3728-3734

ISSN No.:1059-9495

Key Words:dynamic recrystallization; FGH96 superalloy; hot deformation; processing maps

Abstract:The hot deformation behavior of solution and aging FGH96 superalloy were investigated in the deformation temperature range of 1000-1175 degrees C and strain rate range of 0.001-5.0/s on a Gleeble-1500 thermo-mechanical simulator. The results show that the true stress-strain curves are typical of the occurrence of dynamic recrystallization (DRX). The value of the activation energy and materials constants of A and n was obtained through the hyperbolic sine function between the peak stress and Zener-Hollomon parameter. Optical microscopy observations of the grains showed that Zener-Hollomon parameter affected the DRX grain size obviously. In addition, the constitutive equations and DRX kinetics model were also built. The processing maps with the strain of 0.3 and 0.6 were obtained on the basis of dynamic materials model. The results predicted that there existed instability regions at around 1050 degrees C when the strain rate exceeds 0.01/s.