Use of color-change indicators to quantify passive films on the stainless steel valves of nuclear power plants
点击次数：
论文类型：期刊论文
发表时间：2016-02-01
发表刊物：NUCLEAR ENGINEERING AND DESIGN
收录刊物：SCIE、EI
卷号：297
页面范围：267-275
ISSN号：0029-5493
关键字：Materials engineering
摘要：The passive film on nuclear-grade stainless steels was evaluated by quantifying its color changes. Coloration reactions were compared by using ferroin and blue dot solutions as indicators on the basis of the measured results in a laboratory. The reactions were then applied on stainless steel valves in a nuclear power plant. The degree of color change indicates the degree of growth of a passive film. The ferroin solution exhibits higher accuracy and more stable than blue dot solution in determining passive film quality. The potentiodynamic polarization curves show that blue dot solution might cause surface damage compared with ferroin solution. The inspection result on stainless steel valves supports our laboratory result. However, stainless steel exhibited a dramatic decrease in sensitivity to blue dot because of the intrinsic instability and high acidity of this solution. Ferroin solution is superior to blue dot solution for stainless steel facilities in a nuclear power plant. (C) 2015 Elsevier B.V. All rights reserved.
发表时间：2016-02-01