论文名称：Microstructural and mechanical evolutions of sustainable cement blends containing fly ash and calcium carbonate whiskers induced by high temperature 论文类型：期刊论文 发表刊物：CONSTRUCTION AND BUILDING MATERIALS 卷号：263 ISSN号：0950-0618 关键字：Sustainable cement paste; High temperature; Microstructure; Fly ash; Calcium carbonate whisker 摘要：A novel kind of cement blend with high temperature resistance and favorable sustainability was developed in this paper. The physical and chemical changes due to high temperature exposure were examined in this sustainable cement paste containing fly ash (FA) and aragonite calcium carbonate whiskers (CW) as supplementary cementitious materials. High flexural strength is demonstrated before 400 degrees C because FA has pozzolanic effect, self-cementitious properties and potentials to react with CW under hydrothermal condition. When the exposure temperature is above 400 degrees C, especially above 800 degrees C, high residual properties and less deterioration are observed in flexural and compressive strengths and elastic modulus, mainly because FA is involved in the sintering process and formation of ceramic phases. In summary, the sustainable cementitious composites studied in this paper are very promising to have high temperature resistance to reduce fire damage on constructions and at the same time lower carbon dioxide footprint of cement manufacture. (C) 2020 Elsevier Ltd. All rights reserved. 发表时间：2021-01-10