论文名称：Characterization of mechanical behavior and mechanism of calcium carbonate whisker-reinforced cement mortar
论文类型：期刊论文
发表刊物：CONSTRUCTION AND BUILDING MATERIALS
收录刊物：SCIE、EI、Scopus
卷号：66
页面范围：89-97
ISSN号：0950-0618
关键字：Calcium carbonate whisker; Mortar; Fibrous material; Reinforcement; Mechanical property; Reinforcing mechanism
摘要：In order to reinforce cement mortar, a new kind of micro-fibrous material, calcium carbonate whisker (CaCO3 whisker), was incorporated in this study. Microstructure, mechanical properties and reinforcing mechanism of this composite were characterized. It was found that the addition of CaCO3 whisker improved not only the compressive and flexural strength of cement mortar, but also the load-deflection curves and work of fracture. Further work using mercury intrusion porosimetry tests confirmed the filler effect and the refining of the pore distribution of whiskers in cement mortar. Scanning electron microscopy showed that the microscopic mechanism primarily consists of whisker pullout, crack deflection, whisker-cement coalition pullout, whisker bridging and whisker breakage. These mechanisms are related to the matrix strength. As compared to the strong matrix, the weak matrix that was modified with CaCO3 whisker achieved the highest increase in strength and toughness of the cement mortar. This is likely attributed to the crack deflection mechanism, which is weakened by the strong interfacial bonding between the CaCO3 whisker and cement matrix in the stronger mortar matrix. (C) 2014 Elsevier Ltd. All rights reserved.
发表时间：2014-09-15