Journal:JOURNAL OF ALLOYS AND COMPOUNDS

Included Journals:SCIE、EI

Volume:509

Issue:3

Page Number:704-711

ISSN No.:0925-8388

Key Words:Magnesium alloys; Twin roll casting; Microstructure; Mechanical properties

Abstract:Microstructural evolution and mechanical properties of twin roll cast (TRC) Mg-3.3 wt.%Al-0.8 wt.%Mn-0.2 wt.%Ca (AM31 + 0.2Ca) alloy strip during warm rolling and subsequent annealing were investigated in this paper. The as-TRC alloy strip shows columnar dendrites in surface and equiaxed dendrites in center regions, as well as finely dispersed primary Al(8)Mn(5) particles on interdendritic boundaries which result in the beneficial effect on microstructural refinement of strip casting. The warm rolled sheets show intensively deformed band or shear band structures, as well as finely and homogeneously dispersed Al-Mn particles. No evident dynamic recrystallization (DRX) takes place during warm rolling process, which is more likely attributed to the finely dispersed particle and high solid solution of Al and Mn atoms in alpha-Mg matrix. After annealing at 350 degrees C for 1 h, the warm rolled TRC sheets show fine equiaxed grains around 7.8 mu m in average size. It has been shown that the present TRC alloy sheet has superior tensile strength and comparative elongation compared to commercial ingot cast (IC) one, suggesting the possibility of the development of wrought magnesium alloy sheets by twin roll strip casting processing. The microstructural evolution during warm rolling and subsequent annealing as well as the resulting tensile properties were analyzed and discussed. (C) 2010 Elsevier B.V. All rights reserved.