论文名称：Effect of substrate curvature on thickness distribution of polydimethylsiloxane thin film in spin coating process
论文类型：期刊论文
发表刊物：CHINESE PHYSICS B
收录刊物：SCIE
卷号：27
期号：6
ISSN号：1674-1056
关键字：spin coating; non-planar substrate; film thickness distribution; edge-bead effect
摘要：The polymer spin coating is critical in flexible electronic manufaction and micro-electro-mechanical system (MEMS) devices due to its simple operation, and uniformly coated layers. Some researchers focus on the effects of spin coating parameters such as wafer rotating speed, the viscosity of the coating liquid and solvent evaporation on final film thickness. In this work, the influence of substrate curvature on film thickness distribution is considered. A new parameter which represents the edge bead effect ratio (re) is proposed to investigate the influence factor of edge bead effect. Several operation parameters including the curvature of the substrate and the wafer-spin speed are taken into account to study the effects on the film thickness uniformity and edge-bead ratio. The morphologies and film thickness values of the spin-coated PDMS films under various substrate curvatures and coating speeds are measured with laser confocal microscopy. According to the results, both the convex and concave substrate will help to reduce the edge-bead effect significantly and thin film with better surface morphology can be obtained at high spin speed. Additionally, the relationship between the edge-bead ratio and the thin film thickness is like parabolic curve instead of linear dependence. This work may contribute to the mass production of flexible electronic devices.
发表时间：2018-06-01