论文名称：Mechanical properties of Al2O3-SiC-C composites using polycarbosilane as SiC precursor
论文类型：期刊论文
发表刊物：JOURNAL OF ALLOYS AND COMPOUNDS
收录刊物：SCIE、EI、Scopus
卷号：490
期号：1-2
页面范围：484-487
ISSN号：0925-8388
关键字：Al2O3-SiC composites; Polycarbosilane; Mechanical property
摘要：Al2O3-SiC-C composites with varying amounts of SiC were prepared by hot pressing method where polycarbosilane (PCS) adopted as the precursor of SiC. The sintering quality, structure-phase state and mechanical properties of composites were measured and compared with Al2O3 monolithic. It was found that the flexural strength increased from 280 MPa for Al2O3 monolithic to the highest of 520 MPa for a 10wt.% SiC added Al2O3-SiC-C composite, and the fracture toughness was improved from 3.2 to 5.9 MPa m(1/2) at the same time. The reinforcement effects were discussed on considering the addition of SiC phase and free carbon in an Al2O3 composite matrix. (C) 2009 Elsevier B.V. All rights reserved.
发表时间：2010-02-04