Crack healing in SUS304 stainless steel by electropulsing treatment
点击次数：
论文类型：期刊论文
发表时间：2016-02-01
发表刊物：JOURNAL OF CLEANER PRODUCTION
收录刊物：SCIE、EI、Scopus
卷号：113
页面范围：989-994
ISSN号：0959-6526
关键字：Remanufacturing; Crack healing; Electropulsing; Healing area
摘要：The research about repair of metal cracks plays an important role in promoting the development of remanufacturing engineering. Crack in the SUS304 stainless steel was treated by electropulsing with peak current density of 4.1 kA/mm(2). After seven times of electropulsing treatment, continuous healing areas in both left and right side of crack were formed. The process of rapid melting and solidification occurred in healing areas, columnar crystals and fine recrystallization zone were formed at the same time. The detour and joule heating effects were the main reason to realize crack healing and detailed healing processes were discussed. (C) 2015 Elsevier Ltd. All rights reserved.