论文类型：会议论文

发表时间：2010-06-26

收录刊物：EI、CPCI-S、Scopus

卷号：675-677

页面范围：461-+

关键字：ABS; CB; Electrical conductivity; Shielding effectiveness

摘要：In this paper, the effects of carbon black (CB) mass fraction on volume resistivity and electromagnetic shielding effectiveness (SE) of CB/Acrylonitrile Butadiene Styrene (ABS) composites were studied. The results indicated that when CB mass fraction was over 15 wt%, the volume resistivity dropped sharply and when it rose to 35 wt%, the volume resistivity achieved the lowest value about 103 Omega.cm. In addition, there are two obvious percolation effect at 15 similar to 20 wt% and 25 similar to 35 wt% CB respectively in the course of the volume resistivity changing. Titanate coupling agent could greatly improve conduction and SE of CB/ABS composites. Lastly, the SE of CB/ABS composites was investigated by experimental observation.