点击次数：

论文类型：期刊论文

发表时间：2021-01-10

发表刊物：COMPOSITES PART B-ENGINEERING

卷号：199

ISSN号：1359-8368

关键字：MnO2; Core@shell structure; Impedance matching; Broadband microwave absorption

摘要：Building core@shell nanostructures and doping ions are two important strategies to optimize the performance for the microwave impedance matching and attenuation. In this research, the Ag-doped alpha-MnO2@delta-MnO2 was successfully synthesized by combining hydrothermal reaction and chemical deposition reaction. Driven by the lowest surface energy principle, all the delta-MnO2 nanosheets nucleate on the surface of alpha-MnO2 nanowires. During this process, the edge of nanosheets attach on the alpha-MnO2 nanowire with low lattice mismatch of delta (201)//alpha (211) (nearly 0) and vertically grow on the nanowires surfaces, then the assembled core-shell composites can be prepared. The core-shell composites exhibit synergistic effect and improved the impedance matching, so that the absorbing performance has been obtained. The composite shows the minimum reflection loss (RL) of -53.67 dB at 13.28 GHz for 1.8 mm thickness, and the broadest effective absorbing bandwidth (RL < -10 dB) is 5.44 GHz as the thickness was 1.9 mm. The excellent performance is come from the preferable impedance matching, the large heterogeneous existence of the interfaces and the numerous transmission paths for microwave.