Hits:

Indexed by:期刊论文

Date of Publication:2013-07-17

Journal:APPLIED CATALYSIS B-ENVIRONMENTAL

Included Journals:SCIE、EI

Volume:138

Page Number:427-433

ISSN No.:0926-3373

Key Words:Porous silicon; Quantum confinement effect; Photocatalytic oxidation; Stability

Abstract:In this work, hierarchically porous silicon was fabricated through electro-assisted chemical etching using a silicon wafer as a substrate. Pores with an average diameter of ca. 1200 nm (macropores) were observed and a large number of nanopores with a diameter of less than 5 nm were uniformly distributed over the surface of the macropore, forming the hierarchically porous silicon with nanopores in macropores structure (NP-MPSi). UV-vis diffuse reflection measurements indicated that NP-MPSi has a bandgap of 2.12 eV, which is 1.0 eV higher than that of the original silicon wafer because of the quantum confinement effect caused by the nanopores. Mott-Schottky experiments further demonstrated that the increase in bandgap of NP-MPSi arises from a positive shift of the valence band potential, which improves its capability for photocatalytic oxidation. NP-MPSi exhibited higher photoelectrochemical stability than macroporous silicon (MPSi), a comparison sample lacking nanopores. Using phenol as an example, photocatalytic experiments under irradiation with a Xe lamp demonstrated that the kinetic constants of phenol degradation and total organic carbon removal using NP-MPSi were nearly 3.5 and 8.0 times larger, respectively, than those using MPSi. This unique porous silicon material is therefore an attractive photocatalyst for environmental applications. (c) 2013 Elsevier B.V. All rights reserved.