Effect of annealing treatment on the microstructures, mechanical, and wear properties of a manganese brass alloy

点击次数:

论文类型:期刊论文

发表时间:2016-05-28

发表刊物:JOURNAL OF MATERIALS RESEARCH

收录刊物:SCIE、EI

卷号:31

期号:10

页面范围:1491-1500

ISSN号:0884-2914

摘要:The effect of annealing treatment on the microstructures, mechanical, and wear properties of a CuZnAlMnSiNiCr brass alloy is investigated. The results indicate that nanosized Mn5Si3 particles are observed to precipitate from the phase at temperatures above 750 degrees C. After annealing at 800 degrees C for 4 h, the formation of finely, coherent precipitates dispersed within the matrix results in the great improvement of strength, hardness and thus the high wear resistance, which can be proven by the decreased wear rates and friction coefficients. According to the examination of the wear topography, adhesive, abrasive, and oxidative wear are found to be the major wear forms during the dry sliding wear. After the precipitation-hardening treatment, the adhesion and abrasion decrease, and few spallings and cracks are observed on the worn surfaces. In addition, the wear behavior of the alloy is found to be strongly dependent on its strength and hardness.