High temperature deformation of non-directionally solidified Al2O3/YAG/ZrO2 eutectic bulk ceramic: 点击次数：; 发布时间： 2019-03-12; 发布时间：2019-03-12; 论文类型：期刊论文; 发表时间：2017-02-01; 发表刊物：CERAMICS INTERNATIONAL; 收录刊物：EI、SCIE; 卷号：43; 期号：2; 页面范围：1781-1787; ISSN号：0272-8842; 关键字：Microstructure-final; Mechanical properties; Al2O3; Structural applications; 摘要：Excellent high temperature mechanical properties of melt-grown Al2O3-based eutectics have previously been demonstrated in samples prepared by directional solidification methods. In this study, the deformation behaviour of melt-grown Al2O3/YAG/ZrO2 eutectic bulk prepared by a non-directional solidification method was investigated by means of compressive tests in a temperature range of 1200-1700 degrees C. The non-directionally solidified eutectic bulk ceramic has a colony structure and is polycrystalline. It begins to show ductility and has a compressive strength of 320 MPa at 1500 degrees C, which is much higher than that of the sintered ceramic with the same composition. However, its plastic deformability is insufficient, even at 1700 degrees C (just below the melting point of 1715 degrees C), and cracking occurs during compressive deformation.

上一条： The influence of hydrogen on chip formation in cutting Ti-6Al-4V alloys

下一条：Fretting fatigue characteristic of Ti-6Al-4V strengthened by wet peening

副教授博士生导师硕士生导师

性别：男

毕业院校：大连理工大学

学位：博士

所在单位：材料科学与工程学院

学科：材料加工工程

办公地点：大连理工大学铸造中工程心

电子邮箱：