Enhanced Hot Workability of Ti-46Al-4Nb-0.1B Alloy by Introducing Adjustable beta Phase via Elemental Powder Metallurgy
点击次数：
发布时间： 2022-07-12
发布时间：2022-07-12
论文类型：期刊论文
发表时间：2021-03-05
发表刊物：ADVANCED ENGINEERING MATERIALS
卷号：23
期号：1
ISSN号：1438-1656
关键字：beta-elemental powder metallurgy; heat treatment; hot workability; TiAl
摘要：TiAl-base alloys are a kind of promising materials for high-temperature applications. The beta phase existing in TiAl alloy can improve the hot workability, but deteriorates the creep properties. Preparing a beta phase-containing TiAl-base alloy to enhance the hot workability before hot deformation and eliminating the beta/B2 phase by postheat treatment to improve the service performance is a good strategy. Herein, a significant volume fraction of beta phase is obtained in the Ti-46Al-4Nb-0.1B alloy by the elemental powder metallurgy (EPM), and the beta/B2 phase is eliminated by the subsequent heat treatment. The results demonstrate that the microstructure of the EPMed Ti-46Al-4Nb-0.1B alloy predominantly consists of alpha(2)/gamma lamellar colonies, equiaxial gamma grains, and some randomly distributed beta phase and sigma-Nb2Al phase. The beta/B2 phase formed at the Nb-enriched regions is caused by insufficient diffusion. The EPMed Ti-46Al-4Nb-0.1B alloy has a relatively low thermal deformation activation energy (Q, 410 kJ mol(-1)), showed a well hot workability. The existence of the beta phase is advantageous to harmonize the deformation of alpha(2)/gamma lamellar grains and to improve the deformability of the TiAl alloy. The subsequent heat treatment can eliminate the Nb-enriched regions and the B2 phase to ensure good service performance.

付雪松

同专业博导 同专业硕导 个人学术主页

副教授   博士生导师   硕士生导师

性别： 男

毕业院校：大连理工大学

学位： 博士

所在单位：材料科学与工程学院

学科：材料加工工程

办公地点： 大连理工大学铸造中工程心

电子邮箱：

辽ICP备05001357号 地址：中国·辽宁省大连市甘井子区凌工路2号 邮编：116024
版权所有：大连理工大学
访问量： 手机版 English 大连理工大学 登录

开通时间：..

最后更新时间：..