Evolution of interface and tensile properties in 5052 aluminum alloy/304 stainless steel rotary friction welded joint after post-weld heat treatment

论文类型:期刊论文

发表时间:2020-03-01

发表刊物:JOURNAL OF MANUFACTURING PROCESSES

收录刊物:EI、SCIE

卷号:51

页面范围:142-150

ISSN号:1526-6125

关键字:Aluminum/steel rotary friction welded joint; Post-weld heat treatment; Inhomogeneity; Microstructure; Tensile property

摘要:The inhomogeneous properties of 5052 aluminum alloy/304 stainless steel rotary friction welded joint and the growth behavior of intermetallic compound (IMC) layer were investigated. The ultimate tensile strength (UTS) of as-welded joint in 0R location with discontinuous IMC layer reached the maximum value of 203 MPa, and that in R/2 and 3R/4 locations decreased with the increase of IMC layer thickness, but that in R/4 location was the lowest due to the initiation of crack. After post-weld heat treatment at 250 degrees C/20 min, the thickness of IMC layer remained invariant, but the UTS of entire joint increased from 153 MPa to 161.4 MPa. In addition, the difference of UTS along the radius direction decreased, which benefited the engineering application. During post-weld heat treatment at 450 degrees C, the growth of IMC layer in R/4, R/2 and 3R/4 location were faster than that in 0R location. However, the growth of IMC layer deviated from parabolic law, which was attributed to (i) a large number of dislocations, grain boundaries and storage energy in the interface, (ii) the linear growth of Fe4Al13 phase, and (iii) the effect of Cr element.

上一条: Interfacial microstructure and mechanical properties of dissimilar aluminum/steel joint fabricated via refilled friction stir spot welding

下一条: Interfacial microstructure and shear strength of Ti6Al4V alloy/316 L stainless steel joint brazed with Ti33.3Zr16.7Cu50-xNix amorphous filler metals