点击次数：

论文类型：期刊论文

发表时间：2014-09-22

发表刊物：Advanced Materials Research

收录刊物：EI、Scopus

卷号：1017

页面范围：473-478

ISSN号：9783038352211

摘要：In this study, eight nanotwinned cadmium telluride (CdTe or CZ) models were employed to investigate the synergistic and strengthening mechanism of twin boundaries under nanoindentations, using molecular dynamics (MD) simulations. Twin thickness between adjacent boundaries of 16 nm exhibited the maximum hardness during unloading conditions, among eight MD models with twin thickness varied from 4 to 23 nm. The maximum hardness was formed by the synergistic and strengthening effect induced by the stress fields between upper and lower twin boundaries under nanoindentations. When the twin thickness was less than 16 nm, the hardness increased with increasing twin thickness. Whereas, when the twin thickness was more than 16 nm, the hardness decreased with increasing twin thickness. © (2014) Trans Tech Publications, Switzerland.