Hits:

Indexed by:期刊论文

Date of Publication:2009-11-01

Journal:POLYMER DEGRADATION AND STABILITY

Included Journals:SCIE、EI、Scopus

Volume:94

Issue:11

Page Number:2065-2071

ISSN No.:0141-3910

Key Words:Phenyl-s-triazine; Poly(arylene ether)s; Heat-resistant; Solubility; Copolymerization

Abstract:A novel series of soluble and heat-resistant copoly(arylene ether phenyl-s-triazine)s (PAEPs) have been prepared for their potent utilities as structural coatings, high-temperature membranes or adhesives. The copolymers have been synthesized via the nucleophilic displacement polymerization of 2,4-bis(4-fluorophenyl)-6-phenyl-1,3,5-triazine (BFPT) with various ratios of hydroquinone (HQ) and resorcinol (RS). A key feature of these copolymers is the incorporation of multiply meta-ether linkages in the polymer chain, which results in an improvement in the solubility of poly(arylene ether phenyl-s-triazine)s in common organic solvents (e.g., N,N'-dimethylacetamide, N,N'-dimethylformamide, N-methyl-2-pyrrolidinone). The new random copolymers exhibit high glass transitions exceeding 241 degrees C and excellent thermal and thermo-oxidative stabilities associating with decomposition temperatures for 5% mass-loss in excess of 531 degrees C. These copolymers can be easily cast into tough, clear and creasable films and exhibit good mechanical properties. All copolymers are amorphous except PAEP9010 as evidenced by WAXD. Their solubility increases with an increase in meta-ether linkage content in the polymer backbone, while the crystallinity and the overall thermal stability appear to decrease slightly. This kind of phenyl-s-triazine-based poly(arylene ether) copolymers may be considered a good candidate for using as high-performance polymeric materials. (C) 2009 Elsevier Ltd. All rights reserved.