超薄Hastelloy C-276脉冲激光焊接接头的拉伸性能

Hits:

Date of Publication:2013-01-01

Journal:稀有金属材料与工程

Affiliation of Author(s):机械工程学院

Volume:42

Issue:6

Page Number:1241-1245

ISSN No.:1002-185X

Abstract:The pulsed laser welding of 0.5 mm thick Hastelloy C-276 was carried out and the weld joint with less than 1 mm width was obtained, and then the tensile test and XRD analysis were conducted. The results indicate that the yield strength of as-welded sample is nearly the same as that of the base metal, and the tensile strength is just 88.6% of that of the base metal. In the fracture, the enrichment of brittle phase isn't found. Their comparable yield strength is due to the similar effect of solution strengthening of the base metal and grain refining of the as-welded sample. The reduced tensile strength of the welded sample is attributed to the favorable formation of micro-fracture during the tensile test.

Note:新增回溯数据

Pre One:脉冲激光焊脉冲宽度对316L薄板微观组织及显微硬度的影响

Next One:Nd:YAG激光焊接殷钢材料的工艺研究