Indexed by:Journal Papers

Date of Publication:2015-05-30

Journal:APPLIED SURFACE SCIENCE

Included Journals:SCIE、EI

Volume:338

Page Number:126-136

ISSN No.:0169-4332

Key Words:Titanium; Anodization; Fluorination; Superhydrophilic; Superhydrophobic

Abstract:A facile and scalable technique for preparation of superhydrophilic/superhydrophobic titanium (Ti) surface by single-step anodization and fluorination is presented in this paper. The Ti substrates were anodized to produce micro-nano hierarchical structure which is essential for superhydrophilic surface. The water contact angles (WCAs) of 5 mu l water droplets on the anodized Ti surfaces were measured as low as 0 degrees. Capillary rise measurement was used to evaluate the superhydrophilicity on Ti surfaces anodized at different conditions. Results show that higher anodization voltage can yield stronger superhydrophilicity on Ti surface, but the influence of electrolyte temperature on the superhydrophilicity has a close correlation with the anodization voltages. At 20 V and 40 V anodization voltages, the increase of electrolyte temperature can improve the surface superhydrophilicity, but this trend will be reversed when the voltages rise to 60 V and 80 V. Superhydrophobic surfaces were further obtained from fluoroalkylsilane (FAS) modification on the anodized Ti substrates. It was observed that appropriate anodization voltages and electrolyte temperatures can balance the growth and dissolution of the micro-nano hierarchical surface structure, thereby obtaining the desired superhydrophobic Ti surface. The WCA, rolling angle and contact angle hysteresis of water droplets on the best superhydrophobic Ti surface were respectively recorded as 160 degrees, 2 degrees and 1.7 degrees in this work. Furthermore, the superhydrophilic and superhydrophobic Ti surfaces fabricated in this research also show satisfactory stability in acidic, neutral and alkaline aqueous solutions as well as ambient conditions. (C) 2015 Elsevier B.V. All rights reserved.