The influence of the acid source on the structural and anti-oxidation properties of ordered mesoporous carbons
发表时间：2019-03-09
点击次数：
- 论文类型：
- 期刊论文
- 第一作者：
- Hou, Keke
- 通讯作者：
- Guo, XW (reprint author), Dalian Univ Technol, Sch Chem Engn, State Key Lab Fine Chem, Dalian 116024, Peoples R China.
- 合写作者：
- Zhang, Anfeng,Liu, Min,Guo, Xinwen
- 发表时间：
- 2013-01-01
- 发表刊物：
- RSC ADVANCES
- 收录刊物：
- SCIE、Scopus
- 文献类型：
- J
- 卷号：
- 3
- 期号：
- 47
- 页面范围：
- 25050-25057
- ISSN号：
- 2046-2069
- 摘要：
- The synthesis of ordered mesoporous carbons (OMCs) was carried out under acidic aqueous conditions, by cooperative self-assembly of phenol-formaldehyde resol and surfactant F127. The influence of the acid source on the structural and anti-oxidation properties of the OMCs was investigated. The acids (HCl, HNO3, H3PO4 and H2SO4) used in the synthesis are sufficient to induce the self-assembly of resol and F127 to form the mesophase, while the final products carbonized at 600 degrees C show different structural properties. This was mainly due to the different decomposition behaviors of the surfactant during the carbonization process, which depends on the nature of the anions from the acids. After oxidization in acidic (NH4)(2)S2O8 solution, the H3PO4 catalyzed sample undergoes a minimum reduction in surface area and pore volume, and exhibits a larger adsorptive capacity for Co2+, compared with those using HCl and HNO3 as catalyst. This was related to the incorporation of the phosphorus atoms in the sample with H3PO4 as catalyst, which is in favour of increasing the carbonization degree of the sample, and they can also act as adsorptive sites for Co2+.