发表刊物：Virtual and physical prototyping

卷号：14

期号：4

页面范围：371-381

ISSN号：1745-2759

关键字：Additive manufacturing; composite ceramics; Al2O3/Al2TiO5; microstructure; properties

摘要：Al2O3-based composite ceramics have excellent high temperature performance and are ideal materials for preparing hot end components. However, poor fracture toughness and thermal shock resistance limit its applications. Based on the excellent low thermal expansion characteristics and thermal shock resistance of Al2TiO5 ceramic, different composition ratios of Al2O3/Al(2)TiO(5 )composite ceramics were prepared by directed laser deposition (DLD) technology. Effects of TiO2 doping amount on microstructure and properties of the composite ceramics were investigated. Results show that alpha-Al2O3 phase is discretely distributed in the continuous aluminum titanate matrix when TiO2 doping amount between 2 and 30 mol%. With the increase of TiO2 doping amount, content of Al2O3 gradually decreases and its morphology changes from cellular to dendritic. When TiO2 doping amount reaches 43.9 mol%, the microstructure transforms into fine Al2TiO5/Al6Ti2O13 eutectic structure. Property test results show that Al2O3/Al2TiO5 composite ceramics have good comprehensive mechanical properties when TiO2 doping amount between 2 and 6 mol%.