Porous boron doped diamonds as metal-free catalysts for the oxygen reduction reaction in alkaline solution

点击次数:

论文类型: 期刊论文

发表时间: 2018-05-01

发表刊物: APPLIED SURFACE SCIENCE

收录刊物: SCIE、EI

卷号: 439

页面范围: 329-335

ISSN号: 0169-4332

关键字: Porous boron doped diamond; Metal-free catalyst; Electrocatalysis; Oxygen reduction reaction

摘要: Porous boron doped diamonds (BDDs) were obtained on foam nickel substrates with a porosity of 80%, 85%, 90% and 95% respectively by hot filament chemical vapor deposition (HFCVD) technology. Scanning electron microscopy (SEM) reveals that uniform and compact BDDs with a cauliflower-like morphology have covered the overall frame of the foam nickel substrates. Raman spectroscopy shows that the BDDs have a poor crystallinity due to heavily doping boron. X-ray photoelectron spectroscopy (XPS) analysis effectively demonstrates that boron atoms can be successfully incorporated into the crystal lattice of diamonds. Electrochemical measurements indicate that the oxygen reduction potential is unaffected by the specific surface area (SSA), and both the onset potential and the limiting diffusion current density are enhanced with increasing SSA. It is also found that the durability and methanol tolerance of the boron doped diamond catalysts are attenuated as the increasing of SSA. The SSA of the catalyst is directly proportional to the oxygen reduction activity and inversely to the durability and methanol resistance. These results provide a reference to the application of porous boron doped diamonds as potential cathodic catalysts for the oxygen reduction reaction in alkaline solution by adjusting the SSA. (C) 2017 Elsevier B.V. All rights reserved.