发表时间： 2018-03-01

发表刊物： JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY

收录刊物： SCIE、EI、Scopus

卷号： 34

期号： 3

页面范围： 496-502

ISSN号： 1005-0302

关键字： Dielectric loss; Magnetic loss; Spray granulation method; Impedance match

摘要： The microwave absorbents of Fe and C nanoparticles as magnetic loss and dielectric loss material respectively were composited with the polyvinyl alcohol (PVA) as binder by spray granulation method. The electromagnetic parameters of Fe and C composite particles were analyzed by vector network. The complex permittivity and magnetic permeability of Fe and C composite particles matched well with increasing C nanoparticle content, and then the microwave loss property was improved. A minimum reflection loss (RL) of 42.7 dB at 3.68 GHz for a composite with 4.6 mm in thickness can be obtained when the content ratio of the C nanoparticles, the modified Fe nanoparticles and the PVA is 21:49:30 (Sample 3). (C) 2017 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.