点击次数：

论文类型：期刊论文

发表时间：2015-12-01

发表刊物：INTERMETALLICS

收录刊物：SCIE、EI、Scopus

卷号：67

页面范围：138-144

ISSN号：0966-9795

关键字：Metallic glasses; Glass forming ability; Magnetic properties; Rapid solidification; Differential thermal analysis

摘要：The present work is devoted to fabrication of Fe-B-Si-Zr multi-component bulk glassy alloys with good mechanical and soft magnetic properties. Glass formation in Fe-B system is first considered with an empirical cluster-plus-glue-atom model. A basic composition formula [B-B2Fe8]Fe is proposed as the framework for multi-component alloy design. Considering the structural stability of the model glass, Si and Zr are introduced to the [B-B2Fe8] cluster to replace the center B and shell Fe atoms, from which a series of Fe-B-Si-Zr alloys with composition formulas [Si-B2Fe8-xZrx]Fe (x = 0-0.6) are derived. Copper mold casting experiment shows that bulk glassy alloys are formed within the Zr content range of x = 0.2-0.6, and the largest glass-forming ability appears at [Si-B2Fe7.6Zr0.4]Fe with a critical size of 2.5 mm. The bulk glassy alloys exhibit high fracture strength as large as 3850 MPa. Magnetic property measurement indicates that these alloys exhibit good magnetic softness with high saturation magnetization (1.26-1.48 T) and low coercive force (1.6-6.7 A/m). The alloying effects of Si and Zr on bulk glass formation, thermal glass stability and magnetic softness are discussed with the empirical model. (C) 2015 Elsevier Ltd. All rights reserved.