点击次数：

论文类型：期刊论文

发表时间：2012-09-01

发表刊物：MATERIALS & DESIGN

收录刊物：SCIE、EI、Scopus

卷号：40

页面范围：171-175

ISSN号：0261-3069

关键字：Metal matrix; Oxidation; Corrosion

摘要：A new ferrite steel Cr27Mo6Al3Cu with high Mo and low Al is developed, exhibiting excellent oxidation resistance, corrosion resistance, and mechanical property. Alloy rods with a diameter of 10 mm were prepared by copper mold suction-casting method and then solution-treated at 1373 K for 2 h. The experimental results show that this alloy maintains a stable monolithic BCC microstructure. After oxidization at 1373 K for 100 h, a dense and thin oxide layer is generated on the surface of the alloy with the weight gain per unit area G(+) being about 0.4863 g/m(2). Its corrosion-resistant property in 3.5 wt.% NaCl at 298 K is characterized with the corrosion potential E-corr being about -0.091 V, pitting corrosion potential E-b reaching up to 0.867 V. Its mechanical properties are yield tensile strength sigma(0.2) = 523 MPa, ultimate tensile strength sigma(b) = 637 MPa respectively. (C) 2012 Elsevier Ltd. All rights reserved.