点击次数：

论文类型：期刊论文

发表时间：2018-04-01

发表刊物：ADVANCED ENGINEERING MATERIALS

收录刊物：SCIE

卷号：20

期号：4

ISSN号：1438-1656

关键字：Inconel718-NiCrAlY composites; Laser engineered net shaping; Mechanical properties; Microstructure

摘要：Near-defect-free block Inconel718-NiCrAlY composites prepared by laser engineered net shaping are investigated in this study. XRD, SEM, and EDS are applied to analyze the phase composition and microstructure characteristics. The mechanical properties are evaluated by microhardness tester and friction-wear tester. The results show that NiAl brittle intermetallic compounds precipitate in the matrix when NiCrAlY content reaches 60% or more. With the increase of NiCrAlY ratio, the distribution of NiAl changes from intergranular precipitation to intragranular precipitation, and the dendrites growth directions become chaotic. The microhardness of composites improves as the NiCrAlY content rises, reaching to 419 HV for 100%NiCrAlY, and solid solution strengthening has better strengthening effect on microhardness than precipitation strengthening. The wear loss has a clear decrease only when 80% or more NiCrAlY is added, with the maximum wear loss drop of 15.66% for 100%NiCrAlY. The wear mechanisms change from the coexistence of adhesive wear and abrasive wear to mainly abrasive wear with micro brittle fractures when NiCrAlY content is high.