点击次数：

论文类型：期刊论文

发表时间：2019-08-01

发表刊物：JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY

收录刊物：SCIE、EI

卷号：35

期号：8

页面范围：1523-1531

ISSN号：1005-0302

关键字：B4Cp/6061Al composite; Hot-pressing temperature; Microstructure; Mechanical behavior; Reaction product

摘要：B4Cp/6061Al composites have become important structural and functional materials and can be fabricated by powder metallurgy and subsequent hot rolling. In this work, the effects of the hot-pressing temperature on microstructures and mechanical behaviors of the B4Cp/6061Al composites were investigated. The results showed that compared with the T4 heat treated B4Cp/6061Al composite hot pressed at 560 degrees C, the yield strength and failure strain of the composites hot pressed at 580 degrees C were increased to 235 MPa and 18.4%, respectively. This was associated with the interface bonding strength between the B4C particles and the matrix. However, the reaction products, identified to be MgAl2O4 phases, were detected in the composites hot pressed at 600 degrees C. The formation of the MgAl2O4 phases resulted in the Mg depletion, thus reducing the yield strength to 203.5 MPa after the T4 heat treatment due to the effect of the solid solution strengthening being weakened. In addition, the variation of hardness and electrical conductivity was mainly related to the Mg content in the matrix. Based on the as-rolled microstructures observed by SEM, SR-mu CT and fracture surfaces, the deformation schematic diagram was depicted to reflect the tensile deformation process of the composites. (C) 2019 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.