Microstructure and mechanical properties of Mg-5Gd-2Y-2Zn-0.5Zr alloy
- 点击次数：
- 论文类型：期刊论文
- 发表时间：2014-01-01
- 发表刊物：MATERIALS RESEARCH INNOVATIONS
- 收录刊物：SCIE、EI、Scopus
- 文献类型：J
- 卷号：18
- 期号：1
- 页面范围：14-19
- ISSN号：1432-8917
- 关键字：Mg-5Gd-2Y-2Zn-0.5Zr alloy; LPSO structure; Microstructure; Mechanical
properties
- 摘要：Microstructures and mechanical properties of the Mg-5Gd-2Y-2Zn-0.5Zr alloy (wt-%) in the as cast and solution treated conditions have been investigated using optical microscopy, scanning electron microscope, X-ray diffraction, electron probe X-ray microanalyser and transmission electron microscope. The results show that after adding the element Y, the as cast Mg-5Gd-2Y-2Zn-0.5Zr alloy forms the Mg12Zn(Y, Gd) phase with 18R-long period stacking ordered (LPSO) structure, and the Gd atoms in the phase can slow down the transition process of 18R to 14H in high temperature treatment. LPSO phase in the grain boundary can ensure the strength of the alloy at room and elevated temperature through effectively preventing grain boundary sliding. At 250 degrees C, the alloy has shown the similar ultimate tensile strength and tensile yield strength under room temperature, 241 and 130 MPa respectively, and both with excellent elongation.