论文类型：期刊论文
发表时间：2012-04-01
发表刊物：JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION
收录刊物：SCIE、EI、ISTIC
卷号：27
期号：2
页面范围：296-300
ISSN号：1000-2413
关键字：ZnO nanorods; polyfluorene; inorganic-organic hybrid junction; photoluminescence
摘要：The inorganic-organic hybrid junction was synthesized on ITO glass substrate, which was consisted of an n-type ZnO nanorods (NRs) grown by low-temperature aqueous chemical growth method and a p-type polyfluorene (PF) organic film fabricated by spin-coating. The experimental results indicate that densely and uniformly distributed ZnO nanorods are successfully grown on the PF layer. The thickness of the PF layer plays a dominant role for the current voltage (I-V) characteristic of the ZnO NRs/PF inorganic-organic hybrid junction device, and a p-n junction with obviously rectifying behavior is achieved with optimal PF layer thickness. The photoluminescence (PL) spectrum covering the broad visible range was obtained from the n-ZnO nanorods/p-polyfluorene (PF) structure, which was originated from the combination of the PF-related blue emission and the ZnO-related deep level emission.