发表刊物：MATERIALS RESEARCH BULLETIN
收录刊物：SCIE
卷号：43
期号：12
页面范围：3614-3620
ISSN号：0025-5408
关键字：Semiconductors
摘要：The heterojunction light-emitting diode with n-ZnO/p-GaN structure was grown on (0 0 0 1) sapphire Substrate by metalorganic chemical vapor deposition (MOCVD) technique. The heterojunction structure was consisted of an Mg-doped p-type GaN layer with a hole concentration of similar to 10(17) cm(-3) and a unintentionally doped n-type ZnO layer with an electron concentration of similar to 10(18) cm(-3). A distinct blue-violet electroluminescence with a dominant emission peak centered at similar to 415 nm was observed at room temperature from the heterojunction structure under forward bias conditions. The origins of the electroluminescence (EL) emissions are discussed in comparison with the photoluminescence spectra, and it was supposed to be attributed to a radiative recombination in both n-ZnO and p-GaN sides. (C) 2008 Elsevier Ltd. All rights reserved.