发表刊物：VACUUM

收录刊物：SCIE、EI、Scopus

卷号：103

页面范围：33-37

ISSN号：0042-207X

关键字：Boron removal; Slag treatment; Upgraded metallurgical grade Si

摘要：Purification process of MG-Si was limited by the difficulties involved in reducing boron content. The possibility of removing impurity boron (B) in MG-Si using CaO-Al2O3-SiO2-CaF2 slags was investigated in the present study. Different from traditional research methods, the whole melting process was carried out under atmosphere condition, which was closer to the actual production conditions. The thermodynamic and kinetic mechanisms of B removal were analyzed. Based on the ionic structure theory, the relation between ionic structure of slags at high temperature and optical basicity can be explained firstly. The parameters, including the slag optical basicity, melting time and CaF2 content were discussed. The boron content was reduced from original 25 ppmw to 4.4 ppmw through 120 min melting with the optical basicity of 0.551 and 5 wt% CaF2 additions. (C) 2013 Elsevier Ltd. All rights reserved.