RESEARCH ON CHLORIDE ION PENETRATION AND COMPRESSIVE STRENGTH OF OCEAN HIGH PERFORMANCE CONCRETE DOPED WITH NANO-SiO2
点击次数：
论文类型：期刊论文
发表时间：2014-01-01
发表刊物：REVISTA ROMANA DE MATERIALE-ROMANIAN JOURNAL OF MATERIALS
收录刊物：SCIE
卷号：44
期号：3
页面范围：249-256
ISSN号：1583-3186
关键字：nano-SiO2(NS); ocean engineering; high performance concrete(HPC); chloride ion penetration; compressive strength
摘要：The ability to resist at chloride ion penetration and compressive strength of ocean high performance concrete (HPC) with nano-SiO2 (NS) addition was studied. The 6 hours direct current coulometry method (6-hours DC Method) in ASTM C1202-97 was adopted. The experimental results show that the ability to resist at chloride ion penetration of HPC including NS is heightened effectively, the charge through high-performance concrete with 3%, and 5% NS is reduced with 5% and 15% respectively, and the ability to resist at chloride ion penetration can be heightened gradually with of the age; the charge through high-performance concrete with NS decreases with reducing of W/B of concrete.